| Product Introduction | ||||||
| The ePTFE liquid filtration membrane is made of PTFE resin as raw material, and is subjected to a special process, biaxial stretching, to produce a polytetrafluoroethylene hydrophobic film. Then, the original hydrophobic angle of 34 ℃ is modified to 122 ℃ through special chemical and physical modifications. This film has the characteristic of high liquid interception rate through particles above 0.1um. | ||||||
| Product technical parameters | ||||||
| Hydrophilic film series | ||||||
Material number | Weight(g/㎡) | Thickness(mm) | Air permeability(L/㎡.S@500Pa) | Alcohol bubble point(MPa) | Roll length(m) | Microporous particle size(μm) |
| LY-QS-01 | 30-260 | 0.2-0.6 | 12 | 220-280 | 100-300 | 0.1 |
| LY-QS-02 | 30-260 | 0.2-0.6 | 16 | 160-180 | 100-300 | 0.2 |
| LY-QS-04 | 30-260 | 0.2-0.6 | 25 | 60-80 | 100-300 | 0.45 |
| LY-QS-05 | 30-260 | 0.2-0.6 | 40 | 20-40 | 100-300 | 1 |
| Hydrophobic membrane series | ||||||
| Material number | Wide in width(mm) | Thickness(mm) | Air permeability(L/㎡.S@500Pa) | Bubble pressure(MPa) | Velocity of flow(mL/min.c㎡/@1bar) | Microporous particle size(μm) |
| LY-SS-01 | ≤1800 | 30-40 | 10-15 | ≥0.18 | ≥25 | 0.1 |
| LY-SS-02 | ≤1800 | 30-40 | 16-22 | ≥0.13 | ≥45 | 0.2 |
| LY-SS-04 | ≤1800 | 30-40 | 25-35 | ≥0.09 | ≥90 | 0.45 |
| LY-SS-05 | ≤1800 | 30-40 | 65-80 | ≥0.04 | ≥180 | 1 |
| If the above does not meet the requirements, customization can be made according to customer needs. | ||||||
| Advantages of PTFE liquid filtration membrane | ||||||
| ||||||
| Application and field of PTFE liquid filtration membrane | ||||||
| ||||||
| ||||||